Bambu Lab PAHT-CF 3D Printer Filament
Product Features
- Low Moisture Absorption
- Exceptional Mechanical Properties & Layer Adhesion
- High Tensile Strength
- Comes with High Temperature Reusable Spool
- Diameter: 1.75mm +/- 0.03mm
Cautions for Use
- 0.6 mm Nozzle Recommended
- 0.2 mm Nozzle Not Compatible
- Stainless Steel Nozzle Not Recommended
- Dry before Use for the Highest Print Quality
- AMS Compatible
- AMS lite NOT Compatible
- Enclosure Printer Required
Bambu PAHT-CF is a composite of PA12 and carbon fiber. Inheriting the advantages of low water absorption from PA12 and high-performance carbon fiber, Bambu PAHT-CF offers excellent mechanical and thermal properties that can be maintained well even when the prints get wet. Higher Z adhesion layers and flexibility make it ideal for creating engineering parts such as functional prototypes, machining fixtures, injection molds, jigs, and low-volume production parts.
Low water absorption
With a 50% lower water absorption rate compared to normal PA-CF, Bambu PAHT-CF maintains excellent mechanical properties and dimensional stability even when exposed to high humidity.
Mechanical Properties Comparison
|
Normal PA-CF |
PAHT-CF |
Saturated Water Absorption Rate/% ( 25 °C, 55% RH ) |
1.70 |
0.88 |
Bending Strength - XY/MPa (Dry) |
128 |
125 |
Bending Strength - XY/MPa (Wet) |
76 |
115 |
Bending Strength - Z/MPa (Dry) |
48 |
61 |
Bending Strength - Z/MPa (Wet) |
34 |
49 |
Bending Modulus - XY/MPa (Dry) |
4420 |
4230 |
Bending Modulus - XY/MPa (Wet) |
2210 |
3640 |
Bending Modulus - Z/MPa (Dry) |
1470 |
1820 |
Bending Modulus - Z/MPa (Wet) |
770 |
1480 |
Decline rate of mechanical properties after absorbing water/% |
40%-45% |
12%-18% |
*Both PA-CF and PAHT-CF need to be dried at 80 °C for 12 hours before printing.
Exceptional Z-bonding
Bambu PAHT-CF shows much higher adhesion in Z layers compared to normal PA-CF, bringing it the ability to withstand high levels of impact or stress without breaking or deforming.
Z-layer Performance
|
Normal PA-CF |
PAHT-CF |
Improved % |
Bending Strength - Z/MPa |
48 |
61 |
27% |
Bending Modulus - Z/MPa |
1470 |
1820 |
24% |
Impact Strength - Z/(kJ/m²) |
5.7 |
13.3 |
133% |
*Both PA-CF and PAHT-CF need to be dried at 80 °C for 12 hours before printing.
High tensile strength
Bambu PAHT-CF is designed to meet the demands of various industrial and engineering applications where high strength and durability are required.
Designed for high-temperature resistance
The heat deflection temperature of Bambu PAHT-CF is up to 194℃ (0.45MPa)*, making it useful in applications where the printed parts may be exposed to high temperatures without deforming or losing their strength.
*The long-term temperature resistance is related to the structure and usage scenario of the model itself.
Reusable spool
Bambu PAHT-CF comes with a high-temperature resistant spool, which is not prone to deformation in the drying process. Continuing our concept of reducing plastic waste, the spool can also be reused with other Bambu refills.
Accessory Compatibility
|
Recommended |
Not Recommended |
Build Plate |
Smooth PEI Plate, Textured PEI Plate |
Cool Plate SuperTack |
Hotend |
Hotend with Hardened Steel 0.4mm / 0.6mm (recommended) / 0.8 mm |
Hotend with Stainless Steel Nozzle All Size |
Glue |
Glue Stick |
Liquid Glue |
*As the nozzle size increases, the probability of clogging decreases, but the print quality also decreases. Therefore, it is recommended to use a 0.6 mm Hardened Steel nozzle to avoid clogging while maintaining optimal print quality.
RFID for Intelligent Printing
All printing parameters are embedded in RFID, which can be read through our AMS (Automatic Material System).
Load and print! No more tedious setting steps.
Parameters Comparison
|
PET-CF |
PAHT-CF |
Composition |
PET, carbon fiber |
PA 12 and other long-chain PA, carbon fiber |
Hotend Compatibility |
Hardened Steel 0.6 (recommended), 0.4, 0.8 mm |
Build Plate Compatibility |
Engineering Plate, High Temperature Plate, Textured PEI Plate |
Glue |
Glue Stick / Liquid Glue |
Glue Stick |
AMS Compatibility |
NO |
YES |
Print Speed |
< 100 mm/s |
< 100 mm/s |
Toughness (Impact Strength - XY) |
36.0 kJ/m² |
57.5 kJ/m² |
Strength (Bending Strength - XY) |
131 MPa |
125 MPa |
Stiffness (Bending Modulus - XY) |
5320 MPa |
4230 MPa |
Layer Adhesion (Impact Strength - Z) |
4.5 kJ/m² |
13.3 kJ/m² |
Heat Resistant(HDT, 0.45 MPa) |
205 °C |
194 °C |
Saturated Water Absorption Rate / % (25 °C,55% RH) |
0.37 |
0.88 |
Printing Tips
- Drying conditions: 80℃ for 8 hrs. PAHT-CF is highly sensitive to humidity. To achieve optimal printing performance, it is recommeded further drying before use and after storage. For more details please refer to: Filament drying instructions on Bambu Lab's Wiki.
- Bambu PAHT-CF has high thermal insulation requirements during the printing process, making it unsuitable for use with open-frame printers.
- When printing a model with support, we recommend removing the support structures within 2 hours after printing to prevent them from sticking after absorbing moisture. If sticking occurs, dry the model to ease the removal.
- For better print results, please refer to: Printing tips for Engineering materials on Bambu Lab's Wiki.